To design high affinity switchable imaging system,a monomer isobutyl p-styrenesulfonate(IBSS) and its copolymer with styrene(St) and methacrylic acid(MAA) were synthesized.
為了構筑高親和性變化成像體系,合成了p乙烯基苯磺酸異丁酯單體(IBSS),并將其與苯乙烯(St),甲基丙烯酸(MAA)共聚得到一種熱敏樹脂,通過IR1、H NMR、GPC、DSC、TG分別確認了其結構、組成、分子量、熱分解和熱穩(wěn)定性,并采用該樹脂與紅外染料匹配構筑熱敏成像體系。
IA-SSA copolymer,a scale inhibitor,was synthesized from itaconic acid (IA) and styrene sulfonic acid (SSA).
以衣康酸 (IA)和苯乙烯磺酸 (SSA)為原料 ,合成IA/SSA共聚物阻垢劑 ,確定的最佳合成條件 :反應溫度為 10 3℃ ,反應時間為 2h ,引發(fā)劑用量為 7% (占單體總質量 ) ,IA∶SSA質量比為 2 8∶1。
In the aqueous phase,choosing polystyrene sulfonic acid as template doping agent,polyvinyl alcohol as film-forming agent,and aniline as monomer,and utilizing ammonium persulfate to initiate and synthesize the complex solid of PANI/PSSA-PVA,and it's aqueous solution,and then with the method of spin-coating,the corresponding complex electrochromic films is prepared.
在水相中,以聚苯乙烯磺酸(PSSA)為模板摻雜劑,聚乙烯醇(PVA)為成膜助劑,苯胺(An)為單體,過硫酸銨(APS)引發(fā)合成水溶性導電聚苯胺/聚苯乙烯磺酸-聚乙烯醇(PANI/PSSA-PVA)復合物固體及其復合溶液,用旋涂法制備了相應的復合電致變色膜。
Water soluble conductive polyaniline (PAn) was synthesized by the oxidation of aniline(An) doped with ammonium persulfate(APS) and polystyrene sulfonic acid(PSSA) through the method of emulsion polymerization.
以苯胺(An)為單體,過硫酸銨(APS)為引發(fā)劑,采用現(xiàn)場乳液聚合法合成了可完全溶于水的聚苯乙烯磺酸(PSSA)摻雜聚苯胺(PAn)。
OLIGOMERIZATION OF 1-BUTENE III.CATALYST SYSTEM CONTAINING NICKEL p-TOLUENE SULFONATE AND NICKEL POLYSTYRENE SULFONATE
1-丁烯齊聚反應Ⅲ對-甲基苯磺酸鎳及聚苯乙烯磺酸鎳催化體系
Structure and Property Characterization of Cross-linked Polystyrene Sodium Sulfonate
交聯(lián)聚苯乙烯磺酸鈉結構與性能表征
EFFECTS OF PRE-IRRADIATION GRAFTING OF ACRYLIC ACID AND SODIUM STYRENE SULFONATE ON THE PROPERTIES OF FEP MEMBRANES
預輻照接枝丙烯酸、苯乙烯磺酸鈉對聚全氟乙丙烯膜性能的影響
The Inverse Microemulsion Ploymerization of Acrylamide and Sodium Styrene Sulfonate
丙烯酰胺/對苯乙烯磺酸鈉的反相微乳液聚合
Application of Sodium 4-Vinylbenzene Sulfonate in Soap-Free Emulsion Copolymerization of Polysiloxane-Acrylates
苯乙烯磺酸鈉用于硅丙無皂乳液聚合研究
Preparation and Performance of Modified Poly(vinylidene fluoride) Grafted onto a Blended Polystyrene Sulfonated Acid Membrane
改性聚偏氟乙烯接枝共混聚苯乙烯磺酸膜的制備與性能
The Structure and Morphology of the PVDF-g-PSSA Membrane Prepared by the Plain Sodium Silicate(Na_4SiO_4)
改性聚偏氟乙烯接枝苯乙烯磺酸質子導電膜的結構與形貌
Synthesis and Performance of Itaconic Acid-Styrene Sulfonic Sodium-Maleic Anhydride Inhibitor
衣康酸—苯乙烯磺酸鈉—馬來酸酐共聚物的合成及其性能研究
Study on the Preparation and Characterisation of Sodium Styrene Sulfonate Modified Hydrotalcite/ SBR Composites
對苯乙烯磺酸鈉修飾水滑石/丁苯橡膠復合材料的制備與性能研究
Synthesis of the ESA-SSS Copolymer and Determination of Properties Scale Inhibitor
環(huán)氧琥珀酸—對苯乙烯磺酸鈉共聚物的合成及阻垢性能評定
Study on Sodium Polystyrene Sulfonate Drug-resins Liquid Sustained-release System;
聚苯乙烯磺酸鈉藥物樹脂液體緩釋給藥系統(tǒng)的研究
Treatment of Waste Acid from Sulphonation Process in the Production of DSD Acid
乙烯撐二氨基苯磺酸生產中磺化廢酸的處理
Study on Sulfonation Process in the Production of 4, 4'-diaminostilbene-2, 2'-disulfonic Acid and the Treatment of the Waste Sulfuric Acid;
4，4’-二氨基二苯乙烯-2，2’-二磺酸磺化工藝改進及磺化廢酸治理研究
sulfonated polystyrene type resin
磺化聚苯乙烯型樹脂
Synthesis of Sulfonic Groups Functionalized Monodisperse Polystyrene Microspheres via Seeded Polymerization
種子聚合制備表面磺酸基功能化聚苯乙烯微球
Copper(Ⅱ) Trifluoromethanesulfonate Catalyzed Insertion Reaction of Methyl Styryldiazoacetate and Arylamines
三氟甲磺酸銅(Ⅱ)催化的苯乙烯基重氮乙酸甲酯和芳胺的插入反應
New Synthetic Method of Fluorescent Whitening Agent 4,4′-Bis(4-sulfnatostiryl)biphenyl
熒光增白劑4,4′-雙(4-磺酸鈉苯乙烯基)聯(lián)苯新的合成方法
vinyl-sulfonate copolymer
乙烯基磺酸鹽共聚物